Enhancing adhesion of silicon nitride films to carbon-containing oxide films

ABSTRACT

Adhesion between silicon nitride etch-stop layers and carbon doped oxide films may be improved by using plasma argon densification treatments of the carbon doped oxide films. The resulting surface layer of the carbon doped oxide films may be carbon-depleted and may include a relatively rough interface to improve the adhesion of deposited silicon nitride films.

BACKGROUND

[0001] This invention relates generally to adhering silicon nitride films to carbon-containing silicon oxide films.

[0002] In interconnect systems, it is desirable to integrate low dielectric constant interlayer dielectric carbon doped oxide films. Carbon doping of the oxide improves the overall performance of the interconnect system by lowering its dielectric constant. However, the carbon doping also degrades the interface adhesion between the carbon doped oxide interlayer dielectric films and silicon nitride etch-stop films. As a result of the poor adhesion, thermomechanical failures may occur due to packaging induced stress. These failures may occur at the top and bottom of the carbon doped oxide films.

[0003] Current techniques for solving this problem involve using a downstream plasma ammonia pretreatment of the carbon doped oxide film surface before the silicon nitride film deposition. However, this treatment merely removes surface contaminants and does not reduce or solve the adhesion problem.

[0004] Thus, there is a need for better ways to adhere silicon nitride films to carbon-doped oxide films.

BRIEF DESCRIPTION OF THE DRAWINGS

[0005]FIG. 1 is an enlarged cross-sectional view of one embodiment of the present invention;

[0006]FIG. 2 is an enlarged cross-sectional view of the embodiment shown in FIG. 1 in the course of fabrication in accordance with one embodiment of the present invention; and

[0007]FIG. 3 is an enlarged cross-sectional view of the embodiment shown in FIG. 2 in the course of further fabrication in accordance with one embodiment of the present invention.

DETAILED DESCRIPTION

[0008] A directional plasma argon densification treatment of carbon doped oxide films prior to silicon nitride deposition improves the adhesion between the silicon nitride etch-stop film layer and a carbon doped oxide film layer. The densified surface layer creates a buried interface to the bulk carbon doped oxide film. Adhesion between the silicon nitride and the carbon doped oxide film may be improved by more than 50 percent in some embodiments.

[0009] The use of the argon densification process modifies the carbon doped oxide film chemically by producing a carbon-depleted or silicon dioxide-like surface layer. It also modifies the carbon doped oxide film physically by densifying the surface layer. In particular, it creates a rough, buried interface between the dense, carbon-depleted surface layer and the bulk carbon doped oxide film. At the same time, the actual carbon doped oxide surface is not roughened.

[0010] Thus, referring to FIG. 1, the carbon doped oxide film 20 may have a roughened, carbon-depleted surface layer 14 which includes protrusions 16. The silicon nitride etch-stop layer 10 may be formed, for example by deposition, on top of the densified, carbon-depleted surface layer 14.

[0011] Referring to FIG. 2, the substrate may be prepared using the conventional interconnect dual damascene processing where parts of the exposed surface are carbon doped oxide films 20. The top surfaces of the carbon doped oxide films 20 are carbon-rich and relatively porous as a bulk film and the adhesion to the silicon nitride is poor compared to undoped oxide films.

[0012] The entire surface of the carbon doped oxide film 20 may be treated with a directional argon plasma. The power and dose of the argon plasma may be high enough to create a densified, carbon-depleted layer with a buried, rough interface to the bulk films.

[0013] Thus, as shown in FIG. 3, the densified, carbon-depleted surface layer 14 may be created in the carbon doped oxide film 20 resulting in an interface with protrusions 16. Finally, the silicon nitride etch stop layer 10 is formed on the carbon-depleted surface layer 20 as an etch-stop layer for the downstream process steps. The densified, carbon-depleted layer 14 with its roughened interface can enhance the silicon nitride adhesion to the carbon doped oxide films.

[0014] For example, in some embodiments through the use of argon sputtering, the ratio of SiCH₃ to SiOH may be lowered from 0.42 to 0.02 (measured using time-of-flight secondary ion mass spectrometry (TOFSIMS)) on the top five atomic layers), the near surface density may be increased from 1.6 g/cc to 3.9 g/cc (measured with X-ray reflectivity at 20-100 Angstroms) and the roughness of the carbon doped oxide film can be reduced from 0.19 to 0.14 nanometers, measured with atomic force microscopy (AFM). In the same example, the interface adhesion energy may be improved from 3.2 J/m² using ammonia plasma pretreatment or 4.2 j/m² using H₂ plasma to 5.1 J/m² with argon sputtering two times. The fracture interface root mean squared (rms) roughness in nanometers may be improved from 0.23 for ammonia pretreatment or 0.31 for H₂ plasma surface treatment to 0.44 with argon sputtering two times. The adhesion energy may be measured with a 4-point bending on the silicon nitride/carbon doped oxide blanket film stacks. The fracture interface roughness may be measured with an atomic force microscopy of delaminated 4-point bend samples.

[0015] While the present invention has been described with respect to a limited number of embodiments, those skilled in the art will appreciate numerous modifications and variations therefrom. It is intended that the appended claims cover all such modifications and variations as fall within the true spirit and scope of this present invention. 

What is claimed is:
 1. A method comprising: treating a carbon doped oxide film with an argon plasma; and forming a silicon nitride layer over said treated carbon doped oxide film.
 2. The method of claim 1 wherein treating a carbon doped oxide film with an argon plasma includes forming a carbon depleted surface layer.
 3. The method of claim 2 including forming a carbon depleted surface layer with protrusions that extend into the carbon doped oxide film.
 4. The method of claim 1 including forming a densified surface layer.
 5. An integrated circuit comprising: a substrate; a carbon doped oxide film over said substrate, said film having a densified upper surface; and a silicon nitride layer adhered to said carbon doped oxide film on said surface.
 6. The circuit of claim 5 wherein said carbon doped oxide film has protrusions that extend downwardly into said film from said densified upper surface.
 7. The circuit of claim 5 wherein said densified upper surface is carbon depleted.
 8. A method comprising: densifying a carbon doped oxide film; and forming a silicon nitride layer over said densified carbon doped oxide film.
 9. The method of claim 8 including exposing said carbon doped film to an argon plasma.
 10. The method of claim 9 including forming a carbon depleted surface layer on said carbon doped oxide film.
 11. The method of claim 10 including forming protrusions that extend into said carbon doped oxide film from said carbon depleted surface layer.
 12. A method comprising: forming a carbon depleted surface layer on a carbon doped oxide film; and forming a silicon nitride layer over said surface layer of said carbon doped oxide film.
 13. The method of claim 12 wherein said surface of said carbon doped oxide film is densified.
 14. The method of claim 12 including exposing the surface of said carbon doped film to an argon plasma.
 15. The method of claim 12 including forming protrusions that extend into said carbon doped oxide film from said surface layer. 